Fluorescence Spectroscopy to Investigate the Effect of End-tethered Chains and Loops on the Local Glass Transition Temperature of Polystyrene Thin Films Restricted; Files Only

Abstract

I investigated the effect of grafted monocarboxy-terminated polystyrene (PS-COOH) chains and dicarboxy-terminated polystyrene (HOOC-PS-COOH) loops grafted to silica substrates on the local glass transition temperature ($T_g$) of 12 nm thick PS layers intermixed with the grafted polymers, and capped by a 590 nm bulk PS layer. $T_g$ was measured via fluorescence spectroscopy, using pyrene dye copolymerized to PS as the probe. Temperature of the sample was ramped down steadily at 1 $^o$C/min. $T_g$ was located by identifying the change in slope of the linear dependence of fluorescence intensity vs. temperature. Overall, I found that the local $T_g$ next to 50 and 100 kg/mol end-grafted chains increases by approximately $41 \pm 2^o$C independent of the grafting density compared to the $T_g$ next to bare silica substrates, which is equal to $T_{g,bulk}$. These results contributed to a publication with James Merrill, a graduate student of our lab [J.H. Merrill, R. Li and C.B. Roth, \textit{ACS Marco Lett.}, \textbf{2023}, 12, 1-7]. As for the loops, I found that the local $T_g$ next to 50 and 100 kg/mol grafted loops increase by $36 \pm 2 ^o$C and $27 \pm 2 ^o$C compared to $T_{g,bulk}$, respectively, independent of the intermixing time between the 12 nm thick pyrene-labeled PS layer and the grafted loops. In addition, together with a current graduate student in our lab, James Merrill, we found a broad transition when analyzing the intensity vs. temperature data collected over a wide temperature range, which was characterized by identifying a lower $T_g$, denoted as $T_g^{mid}$. $T_g^{mid}$ is still elevated compared to $T_{g,bulk}$, and is around $115 ^o$C next to 50 and 100 kg/mol grafted loops, and varies between $113 ^o$C and $130 ^o$C for 50 and 100 kg/mol grafted chains. The difference $\Delta T_g = T_g - T_g^{mid}$ may inform about the breadth of glass transition, but its physical significance is yet to be determined.

Table of Contents

Chapter 1: Introduction and Background.......................... 1

1.1 Introduction of Polymers and the Polymer Glass Transition . . . . . . . . . . . . . 1

1.2 The Effect of a Modified Interface on the Polystyrene Glass Transition Temperature .....4

1.2.1 Literature of How Grafted Chains Impact Polystyrene Glass Transition . . . 5

1.2.2 Impact of How Adsorbed Layers Impact the Polystyrene Glass Transition . 7

1.2.3 Summary of Previous Literature ....................... 10

1.3 Goals of the Project.................................. 10 

Chapter 2: Experimental Methods.............................. 12

2.1 Preparation of the Multilayer Sample......................... 12

2.1.1 Preparation of Grafted Layers ........................ 12

2.1.2 Preparation of Pyrene-labeled PS Layer, the Bulk PS Layer and Their Assembly..................................... 14

2.1.3 Measuring the Thicknesses of the Layers via Ellipsometry . . . . . . . . . 15

2.2 Fluorescence Spectroscopy to Probe the Glass Transition Temperature . . . . . . . 17

2.3 Our Fluorescence Spectroscopy Method of Sensing the Glass Transition . . . . . . 21 

Chapter3: Results and Discussion.............................. 25

3.1 Control Experiments ................................. 25

3.2 Effect of End-Grafted Chains and Loops on the Local Glass Transition Temperature ..........27

3.2.1 Effect of Grafted Chains on the Local Glass Transition Temperature . . . . 27

3.2.2 Effect of Grafted Loops on the Local Glass Transition Temperature . . . . 30

3.3 Discovery of Broad Glass Transition Over Extended Temperature Range . . . . . . 34

3.3.1 The ”Midpoint” Glass Transition Temperature of Grafted Chains . . . . . . 37

3.3.2 The Midpoint Glass Transition Temperature of Grafted Loops . . . . . . . 37 

Chapter 4: Conclusion and Further Works ......................... 40

4.1 Summary of the Results................................ 40

4.2 The Next Steps of the Project............................. 41

References ........................................... 43 

About this Honors Thesis

Rights statement

• Permission granted by the author to include this thesis or dissertation in this repository. All rights reserved by the author. Please contact the author for information regarding the reproduction and use of this thesis or dissertation.

School	Emory College
Department	Physics
Degree	B.S.
Submission	Honors Thesis
Language	English
Research Field	Physics, Condensed Matter Chemistry, Polymer
Parola chiave	Grafted layer Polystyrene glass transition
Committee Chair / Thesis Advisor	Connie B. Roth, Emory University
Committee Members	Jed Brody, Emory University Jennifer Rieser, Emory University

Ultima modifica

Primary PDF

Thumbnail	Title	Date Uploaded	Actions
	File download under embargo until 24 May 2025	2024-04-06 14:17:45 -0400	File download under embargo until 24 May 2025

Supplemental Files

Thumbnail	Title	Date Uploaded	Actions